DC: external dimensions: f20 x 86 mm, weight: 50g. The impact device is short and is mainly used in very tight places such as holes or cylinders D + 15: dimensions: f20 x 162 mm, weight: 80 g. Small head for measuring the hardness of grooves or concave surfaces C: Total dimensions: f20 x 141 mm, weight: 75 g. Minimal impact energy, for measuring small, light, thin parts and surface-hardened layers G: Total dimensions: f30 x 254 mm, weight: 250 g. High impact energy, low requirements on the measuring surface. For large, heavy forgings with rough surface E: Dimensions: f20 x 162, weight 80g. The penetration body is made of artificial diamond. It is used to determine extremely hard materials › See more product details; Product description Leeb Hardness Tester D Impact Body The main features of other types of impact devices are the Leeb hardness testers DC, D + 15, C, G, E and DL. DL: Dimensions: f20 x 202 mm, weight: 80 g. The head is thinner and is used for measuring the hardness of narrow grooves and gear surfaces. Material: Procedure impact device D/DC t+15 CGE DL Steel and cast steel. HRC 20-68.5 19.3-67.9 20.0-69.5. 22.4-70.7 20.6-68.2 HRB 38.4-99.6 12.5-39.9 37.0-99.9. HRA 59.1-85.8 61.7-88.0. HB 127-651 80-638 80-683 90-646 cm 83-663 81-646 HV 83-976 80-937 80-996 84-1042 80-950 cm HS 32.2-99.5 33.3-99.3 31.8-102.1 35.8-102.6 30.6-96.8 cold work Tool steel. HRC 20.4-67.1 19.8-68.2 20.7-68.2 22.6-70.2 HV 80-898 80-935 100-941 82-1009 Stainless steel HRB 46.5-101.7 HB 85-655 HV 85-802 Grey cast iron. HRC HB 93-334 92-326 cm HV Ductile iron HRC HB 131-387 127-364 cm HV Cast aluminium alloys HB 19-164 cm 23-210 cm 6/168 cm HRB 23.8-84.6 22.7-85.0. 23.8-85.5 Brass (copper-zinc alloys). HB 40/173 cm HRB 13.5-95.3 Bronze (copper-aluminium/tin alloys). HB 60-290 cm Copper kneading alloys HB 45-315 Available impact equipment types DC: test hole or hollow cylinder. T+15: Test groove or penetrating surface. C: Test small, light, thin parts and the surface of the hardened layer. G: Test large, thick, heavy steels with rough finish E: Test materials with very high hardness DL: test a narrow groove or hole Test conditions: Impact Device Type DC(D)/DL t+15 CGE Influential energy Impact Body Mass 11 mJ. 5.5g/7.2g 11 mJ. 7.8 g. 2.7 mJ. 3.0 g; Product description Leeb Hardness Tester D Impact Body The main features of other types of impact devices are the Leeb hardness testers DC, D + 15, C, G, E and DL. DL: Dimensions: f20 x 202 mm, weight: 80 g. The head is thinner and is used for measuring the hardness of narrow grooves and gear surfaces. Material: Procedure impact device D/DC t+15 CGE DL Steel and cast steel. HRC 20-68.5 19.3-67.9 20.0-69.5. 22.4-70.7 20.6-68.2 HRB 38.4-99.6 12.5-39.9 37.0-99.9. HRA 59.1-85.8 61.7-88.0. HB 127-651 80-638 80-683 90-646 cm 83-663 81-646 HV 83-976 80-937 80-996 84-1042 80-950 cm HS 32.2-99.5 33.3-99.3 31.8-102.1 35.8-102.6 30.6-96.8 cold work Tool steel. HRC 20.4-67.1 19.8-68.2 20.7-68.2 22.6-70.2 HV 80-898 80-935 100-941 82-1009 Stainless steel HRB 46.5-101.7 HB 85-655 HV 85-802 Grey cast iron. HRC HB 93-334 92-326 cm HV Ductile iron HRC HB 131-387 127-364 cm HV Cast aluminium alloys HB 19-164 cm 23-210 cm 6/168 cm HRB 23.8-84.6 22.7-85.0. 23.8-85.5 Brass (copper-zinc alloys). HB 40/173 cm HRB 13.5-95.3 Bronze (copper-aluminium/tin alloys). HB 60-290 cm Copper kneading alloys HB 45-315 Available impact equipment types DC: test hole or hollow cylinder. T+15: Test groove or penetrating surface. C: Test small, light, thin parts and the surface of the hardened layer. G: Test large, thick, heavy steels with rough finish E: Test materials with very high hardness DL: test a narrow groove or hole Test conditions: Impact Device Type DC(D)/DL t+15 CGE Influential energy Impact Body Mass 11 mJ. 5.5g/7.2g 11 mJ. 7.8 g. 2.7 mJ. 3.0 g; Leeb Hardness Tester D Impact Body The main features of other types of impact devices are the Leeb hardness testers DC, D + 15, C, G, E and DL. DL: Dimensions: f20 x 202 mm, weight: 80 g. The head is thinner and is used for measuring the hardness of narrow grooves and gear surfaces. Material: Procedure impact device D/DC t+15 CGE DL Steel and cast steel. HRC 20-68.5 19.3-67.9 20.0-69.5. 22.4-70.7 20.6-68.2 HRB 38.4-99.6 12.5-39.9 37.0-99.9. HRA 59.1-85.8 61.7-88.0. HB 127-651 80-638 80-683 90-646 cm 83-663 81-646 HV 83-976 80-937 80-996 84-1042 80-950 cm HS 32.2-99.5 33.3-99.3 31.8-102.1 35.8-102.6 30.6-96.8 cold work Tool steel. HRC 20.4-67.1 19.8-68.2 20.7-68.2 22.6-70.2 HV 80-898 80-935 100-941 82-1009 Stainless steel HRB 46.5-101.7 HB 85-655 HV 85-802 Grey cast iron. HRC HB 93-334 92-326 cm HV Ductile iron HRC HB 131-387 127-364 cm HV Cast aluminium alloys HB 19-164 cm 23-210 cm 6/168 cm HRB 23.8-84.6 22.7-85.0. 23.8-85.5 Brass (copper-zinc alloys). HB 40/173 cm HRB 13.5-95.3 Bronze (copper-aluminium/tin alloys). HB 60-290 cm Copper kneading alloys HB 45-315 Available impact equipment types DC: test hole or hollow cylinder. T+15: Test groove or penetrating surface. C: Test small, light, thin parts and the surface of the hardened layer. G: Test large, thick, heavy steels with rough finish E: Test materials with very high hardness DL: test a narrow groove or hole Test conditions: Impact Device Type DC(D)/DL t+15 CGE Influential energy Impact Body Mass 11 mJ. 5.5g/7.2g 11 mJ. 7.8 g. 2.7 mJ. 3.0 g
|
![Pack of 10 Dimmable G9 Halogen Bulbs, 40 W 230 V 2800 K G9 Halogen Bulbs for Oven Lamp, Ceiling Lights, Candlesticks [Energy Class F]](https://anete.shop/image/cache/catalog/ext4oc/90/19083374_-9007480-238x238.jpg)
